Evolution law of directional solidification structure of Nb42Ti21Co37 ternary quasiperitectic alloy
Author:
Affiliation:

Clc Number:

Fund Project:

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    The quasiperitecticcoated transformation has the dual characteristics of eutectic transformation and peritectic transformation, and it exists in many industrial alloys. However, a relatively complete theoretical model of peritectic solidification has not been established so far, and there are few related studies on its solidification mechanism. Based on this, this article carried out directional solidification experiments at different drawing speeds (v=1, 3, 5, 15, 30, 70 μm/s) for the Nb42Ti21Co37 quasiperitectic alloy, aiming to study the alloy"s performance at different drawing speeds. Microstructure evolution law, and build the corresponding solidification mechanism. The research results show that the conventional as-cast and directional solidification structures of Nb42Ti21Co37 quasiperitectic alloy contain α-Nb,Co6Nb7 and TiCo+Co6Nb7 quasiperitectic phases. With the gradual increase of the drawing rate, the primary α-Nb phase undergoes a spherical shape →petal-like →cluster-like →dendrite-like transformation; along with the above process, the quenched interface has undergone the transformation from cellular interface to cellular dendrite-like interface, and at the pulling rate v=70 μm/s, solid/liquid The interface disappears; secondly, the quasiperitectic structure in the steady-state growth zone of directional solidification is gradually refined, and the interlayer spacing has an exponential linear relationship with the growth rate, that is, λ=1+5×e2.5V;when the pulling rate is lower than 5μm/s the directional solidification process of the alloy is similar to equilibrium solidification; in addition, the growth mechanism of each phase in the stable growth zone is symbiotic growth. With the increase of the pulling rate, the directional arrangement of the quasiperitectic structure gradually deteriorates.

    Reference
    Related
    Cited by
Get Citation

[Wang Jinhua,闫二虎,Di Chongbo, Chen Yuncan, Liu Wei, Wang Hao, Ge Xiaoyu, Cheng Jian, Huang Renjun, Sun Lixian. Evolution law of directional solidification structure of Nb42Ti21Co37 ternary quasiperitectic alloy[J]. Rare Metal Materials and Engineering,2021,50(10):3577~3584.]
DOI:10.12442/j. issn.1002-185X.20200786

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:October 12,2020
  • Revised:December 11,2020
  • Adopted:December 22,2020
  • Online: October 28,2021
  • Published: October 25,2021